TGG
Main Properties：
| Chemical Formula |
Tb3Ga5O12 |
| Lattice Parameter |
a=12.355Å |
| Growth Method |
Czocralski |
| Density |
7.13g/cm3 |
| Mohs Hardness |
8.0 |
| Melting Point |
1725 ℃ |
| Refractive Index |
1.954 at 1064nm |
| Chemical Formula | Tb3Ga5O12 |
| Lattice Parameter | a=12.355Å |
| Growth Method | Czocralski |
| Density | 7.13g/cm3 |
| Mohs Hardness | 8.0 |
| Melting Point | 1725 ℃ |
| Refractive Index | 1.954 at 1064nm |
Standard TGG Rod Specification:
| Orientation |
[111] within ±15 arc min |
| Wave Front Distortion |
< 1/8 wave |
| Extinction Ratio |
> 30dB |
| Diameter |
+0.00mm/-0.05mm |
| Length |
+0.2mm/-0.2mm |
| Chamfer |
0.10mm @ 45° |
| Flatness |
< 1/10 wave at 633nm |
| Parallelism |
< 30 arc Seconds |
| Perpendicularity |
< 5 arc min |
| Surface Quality |
10/5 Scratch/Dig |
| AR coating |
<0.2% |
| Orientation | [111] within ±15 arc min |
| Wave Front Distortion | < 1/8 wave |
| Extinction Ratio | > 30dB |
| Diameter | +0.00mm/-0.05mm |
| Length | +0.2mm/-0.2mm |
| Chamfer | 0.10mm @ 45° |
| Flatness | < 1/10 wave at 633nm |
| Parallelism | < 30 arc Seconds |
| Perpendicularity | < 5 arc min |
| Surface Quality | 10/5 Scratch/Dig |
| AR coating | <0.2% |